Contact pressure of porous Al2O3 probed by nanoindentations
Ling Z(凌中); Hao SW(郝圣旺); Ling Z
Source PublicationStructural Integrity And Failure
2008
Pages69-74
Conference NameInternational Conference on Structural Integrity and Failure/International Conference on Failure Analysis and Maintenance Technologies
Conference DateJUL 09-11, 2008
Conference PlacePerth, AUSTRALIA
AbstractContact pressure of porous Al2O3 probed by nanoindentation was investigated by dimensional analysis with special attention paid to scaling effects in the mechanical behavior. It was found that, for sample containing small grains and interconnected pores, the contact pressure is manifest dominated by bonding strength of the porous alumina. Whereas the samples with coarse grain and various porous structures exhibit higher contact pressures and smaller residual deformations, which can be attributed to the mechanical response of the solid-phase under current limited peak loads.
KeywordPorous Al2o3 Contact Pressure Microscale Nanoindentation Indentation Modulus Alumina Strength
WOS IDWOS:000257176700011
ISBN978-0-87849-386-9
URL查看原文
Indexed ByCPCI-S
Language英语
Citation statistics
Document Type会议论文
Identifierhttp://dspace.imech.ac.cn/handle/311007/25392
Collection力学所知识产出(1956-2008)
Corresponding AuthorLing Z
Recommended Citation
GB/T 7714
Ling Z,Hao SW,Ling Z. Contact pressure of porous Al2O3 probed by nanoindentations[C]Structural Integrity And Failure,2008:69-74.
Files in This Item: Download All
File Name/Size DocType Version Access License
AMR.41-42.69.pdf(600KB) 开放获取--View Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Lanfanshu
Similar articles in Lanfanshu
[Ling Z(凌中)]'s Articles
[Hao SW(郝圣旺)]'s Articles
[Ling Z]'s Articles
Baidu academic
Similar articles in Baidu academic
[Ling Z(凌中)]'s Articles
[Hao SW(郝圣旺)]'s Articles
[Ling Z]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Ling Z(凌中)]'s Articles
[Hao SW(郝圣旺)]'s Articles
[Ling Z]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: AMR.41-42.69.pdf
Format: Adobe PDF
This file does not support browsing at this time
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.