| On The Thermally Induced Cracking Of A Segmented Coating Deposited On The Outer Surface Of A Hollow Cylinder | |
Chen XJ(陈学军) ; Chen GN(陈光南); Chen XJ
| |
| Source Publication | Surface & Coatings Technology
 |
| 2009 | |
| Volume | 203Issue:9Pages:1114-1120 |
| ISSN | 0257-8972 |
| Abstract | In this work, the thermally induced cracking behavior of a segmented coating has been investigated. The geometry under consideration is a hollow cylinder with a segmented coating deposited onto its outer surface. The segmentation cracks are modeled as a periodic array of axial edge cracks. The finite element method is utilized to obtain the solution of the multiple crack problem and the Thermal Stress Intensity Factors (TSIFs) are calculated. Based on dimensional analysis, the main parameters affecting TSIFs are identified. It has been found that the TSIF is a monotonically increasing function of segmentation crack spacing. This result confirms that a segmented coating exhibits much higher thermal shock resistance than an intact counterpart, if only the segmentation crack spacing is narrow enough. The dependence of TSIF on some other parameters, such as normalized time, segmentation crack depth, convection severity as well as material constants, has also been discussed. (C) 2008 Elsevier B.V. All rights reserved. |
| Keyword | Segmented Coating Cracking Thermal Stress Intensity Factor (Tsif) Finite Element Method Thick-walled Cylinder Barrier Coatings Axial Cracks Shock Fracture Delamination Stability |
| DOI | 10.1016/j.surfcoat.2008.10.002 |
| Indexed By | SCI |
| Language | 英语 |
| WOS ID | WOS:000263388200002 |
| WOS Keyword | THICK-WALLED CYLINDER ; BARRIER COATINGS ; AXIAL CRACKS ; SHOCK ; FRACTURE ; DELAMINATION ; STABILITY |
| WOS Research Area | Materials Science ; Physics |
| WOS Subject | Materials Science, Coatings & Films ; Physics, Applied |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://dspace.imech.ac.cn/handle/311007/26738 |
| Collection | 先进制造工艺力学实验室 |
| Corresponding Author | Chen XJ |
| Recommended Citation GB/T 7714 | Chen XJ,Chen GN,Chen XJ. On The Thermally Induced Cracking Of A Segmented Coating Deposited On The Outer Surface Of A Hollow Cylinder[J]. Surface & Coatings Technology,2009,203,9,:1114-1120. |
| APA | 陈学军,陈光南,&Chen XJ.(2009).On The Thermally Induced Cracking Of A Segmented Coating Deposited On The Outer Surface Of A Hollow Cylinder.Surface & Coatings Technology,203(9),1114-1120. |
| MLA | 陈学军,et al."On The Thermally Induced Cracking Of A Segmented Coating Deposited On The Outer Surface Of A Hollow Cylinder".Surface & Coatings Technology 203.9(2009):1114-1120. |
| Files in This Item: | Download All | |||||
| File Name/Size | DocType | Version | Access | License | ||
| Jp069.pdf（1070KB） | 开放获取 | -- | View Download | |||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment