| Grain Refinement of Hypereutectic Immiscible Cu-50Cr Alloy during Rapid Melting and Solidification Induced by High Power Density Laser Beams | |
Zhang LT(张犁天); Yu G(虞钢) ; Tian CX(田崇鑫); He XL(何秀丽); Li SX(李少霞)
| |
| Corresponding Author | Yu, Gang([email protected]) |
| Source Publication | METALS
 |
| 2019-05-01 | |
| Volume | 9Issue:5Pages:19 |
| ISSN | 2075-4701 |
| Abstract | The microstructure of hypereutectic immiscible Cu-50Cr alloy (wt%) was effectively refined and homogenized by a high power density Nd:YAG continuous laser beam (power density 10(4)-10(5) MW/m(2)). The average grain size of Cr was effectively refined from similar to 100 mu m to similar to 1 mu m, and some of the Cr particles even decreased to a few hundred nanometers. The high cooling rate (7.29 x 10(6) K/s) effectively inhibited the coarsening effect on Cr particles during liquid phase separation (LPS). The spherical Cr particles were preferably dispersed in the melt layer, and the thickness of the layer was up to similar to 150 mu m. The refinement and dispersion of the Cr phase contributed to improving the interruption capability of the Cu-Cr contacts. Compared with the untreated samples, the arc duration and the withstanding voltage of the laser surface melting (LSM) treated contacts with refined microstructure increased to 21% and 33%, respectively. The results demonstrated that the LSM method was an effective approach to optimize the microstructure of Cu-Cr alloy, which made it a promising modification method for Cu-Cr vacuum contact applications. |
| Keyword | Cu-Cr immiscible alloy laser surface melting (LSM) liquid phase separation (LPS) grain refinement rapid solidification interruption capability |
| DOI | 10.3390/met9050585 |
| Indexed By | SCI |
| Language | 英语 |
| WOS ID | WOS:000478818700102 |
| WOS Keyword | LIQUID-PHASE SEPARATION ; CU-CR ALLOYS ; COOLING RATE ; MICROSTRUCTURE ; COPPER ; CHROMIUM ; TRANSFORMATION ; RESISTANCE ; VOLTAGE |
| WOS Research Area | Materials Science ; Metallurgy & Metallurgical Engineering |
| WOS Subject | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| Funding Project | Chinese Academy of Sciences[yz201636] ; Beijing Municipal Commission of Science and Technology[Z181100003818015] |
| Funding Organization | Chinese Academy of Sciences ; Beijing Municipal Commission of Science and Technology |
| Classification | 二类/Q1 |
| Ranking | 1 |
| Contributor | Yu, Gang |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://dspace.imech.ac.cn/handle/311007/79757 |
| Collection | 先进制造工艺力学实验室 |
| Recommended Citation GB/T 7714 | Zhang LT,Yu G,Tian CX,et al. Grain Refinement of Hypereutectic Immiscible Cu-50Cr Alloy during Rapid Melting and Solidification Induced by High Power Density Laser Beams[J]. METALS,2019,9,5,:19.Rp_Au:Yu, Gang |
| APA | 张犁天,虞钢,田崇鑫,何秀丽,&李少霞.(2019).Grain Refinement of Hypereutectic Immiscible Cu-50Cr Alloy during Rapid Melting and Solidification Induced by High Power Density Laser Beams.METALS,9(5),19. |
| MLA | 张犁天,et al."Grain Refinement of Hypereutectic Immiscible Cu-50Cr Alloy during Rapid Melting and Solidification Induced by High Power Density Laser Beams".METALS 9.5(2019):19. |
| Files in This Item: | Download All | |||||
| File Name/Size | DocType | Version | Access | License | ||
| Jp2019314.pdf（5098KB） | 期刊论文 | 出版稿 | 开放获取 | CC BY-NC-SA | View Download | |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment