The effect of porosity size and oxidation on the HCF property of nickel-based single crystal superalloy at 980 degrees C

doi:10.1016/j.tafmec.2022.103423

IMECH-IR > 非线性力学国家重点实验室

	The effect of porosity size and oxidation on the HCF property of nickel-based single crystal superalloy at 980 degrees C
	Jiang, Wen 1,2; Li, Piao 3; Yao, Wei-Xing 3; Rui SS(芮少石)4,5; Shi, Hui-Ji 5; Huang, Jie 3
通讯作者	Jiang, Wen([email protected])
发表期刊	THEORETICAL AND APPLIED FRACTURE MECHANICS
	2022-08-01
卷号	120 页码:16
ISSN	0167-8442
摘要	The high-cycle fatigue (HCF) lives and fatigue limits of nickel-based single crystal superalloys (NBSX) with different porosity sizes were investigated at 980 degrees C. The test results show that the failure cracks prone to initiate from large internal pores, and the HCF properties are mainly controlled by the critical pore size. However, when the stress is close to the fatigue limit, the secondary cracks will initiate from the oxide layer obviously, which will further weaken the HCF properties. Therefore, a life prediction model based on the critical plane parameter and oxidation kinetic equation was proposed to evaluate the effect of porosity size and oxidation on the HCF life of NBSX. Then, combing the life prediction model and Murakami model, a fatigue limit evaluation model was presented. Compared with test results, the life prediction model and fatigue limit evaluation model are accurate and effective. Finally, the defect-tolerance analysis was carried out by the Kitagawa-Takahashi diagram, which could be a visual guide for the anti-fatigue design of NBSX.
关键词	Nickel-based single crystal superalloys High-cycle fatigue life Fatigue limit Porosity size Oxidation
DOI	10.1016/j.tafmec.2022.103423
收录类别	SCI ; EI
语种	英语
WOS记录号	WOS:000813362000003
关键词[WOS]	HIGH-CYCLE FATIGUE ; NON-METALLIC INCLUSIONS ; HIGH-STRENGTH STEELS ; THERMOMECHANICAL FATIGUE ; QUANTITATIVE-EVALUATION ; COMPUTED-TOMOGRAPHY ; CRACK INITIATION ; LIFE PREDICTION ; BEHAVIOR ; TEMPERATURE
WOS研究方向	Engineering ; Mechanics
WOS类目	Engineering, Mechanical ; Mechanics
资助项目	National Major Science and Tech- nology Project of China[2017 -VI -0003-0073] ; National Natural Science Foundation of China[52075244] ; National Natural Science Foundation of China[52002181] ; Priority Academic Program Development of Jiangsu Higher Education Institutions[1108007002]
项目资助者	National Major Science and Tech- nology Project of China ; National Natural Science Foundation of China ; Priority Academic Program Development of Jiangsu Higher Education Institutions
论文分区	二类/Q1
力学所作者排名	3+
RpAuthor	Jiang, Wen
引用统计	被引频次：14[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://dspace.imech.ac.cn/handle/311007/89683
专题	非线性力学国家重点实验室
作者单位	1.Nanjing Engn Inst Aircraft Syst, AVIC, Nanjing 211106, Peoples R China; 2.Aviat Key Lab Sci & Technol Aero Electromech Syst, Nanjing 211106, Peoples R China; 3.State Key Lab Mech & Control Mech Struct, Nanjing 210016, Peoples R China; 4.Chinese Acad Sci, Inst Mech, LNM, Beijing 100190, Peoples R China; 5.Tsinghua Univ, Sch Aerosp Engn, AML, Beijing 100084, Peoples R China
推荐引用方式 GB/T 7714	Jiang, Wen,Li, Piao,Yao, Wei-Xing,et al. The effect of porosity size and oxidation on the HCF property of nickel-based single crystal superalloy at 980 degrees C[J]. THEORETICAL AND APPLIED FRACTURE MECHANICS,2022,120:16.Rp_Au:Jiang, Wen
APA	Jiang, Wen,Li, Piao,Yao, Wei-Xing,芮少石,Shi, Hui-Ji,&Huang, Jie.(2022).The effect of porosity size and oxidation on the HCF property of nickel-based single crystal superalloy at 980 degrees C.THEORETICAL AND APPLIED FRACTURE MECHANICS,120,16.
MLA	Jiang, Wen,et al."The effect of porosity size and oxidation on the HCF property of nickel-based single crystal superalloy at 980 degrees C".THEORETICAL AND APPLIED FRACTURE MECHANICS 120(2022):16.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Jp2022FA234_2022_The（16273KB）	期刊论文	出版稿	开放获取	CC BY-NC-SA	浏览下载