| Effects of Natural Aging and Discontinuous Cyclic Loading on High Cycle Fatigue Behavior of Steels | |
Li G(李根); Liu, Jiajun1; Sun, Jian1 ; Sun CQ(孙成奇)
| |
| Source Publication | METALS
 |
| 2023-03 | |
| Volume | 13Issue:3Pages:511 |
| Abstract | Metallic components may not be used immediately and are stored for several months or years after fabrication in some cases, which experience long term natural aging. Moreover, the fatigue beared components commonly suffer discontinuous cyclic loadings in service. In this paper, the effects of natural aging and discontinuous loading on high cycle fatigue life and failure mechanism were investigated through rotating bending fatigue tests. The long term natural aging (e.g., more than 20,000 h) reduced the fatigue life of both 25CrMo4 and 30CrMnSiA steels, and this effect was irrespective of the roughness of the specimen surface. The effect of natural aging on the failure mechanism was related to the microstructure of materials. The natural aging promoted the probability of multi site crack initiation for 25CrMo4 steel, but had no influence on the crack initiation mode of 30CrMnSiA steel. The discontinuous cyclic loading had no harmful influence on the fatigue life of 25CrMo4 steel, and it had no influence on the failure mechanism. The specimens under continuous and discontinuous cyclic loadings both failed from single site crack initiation or multi site crack initiation at the specimen surface. |
| Keyword | natural aging discontinuous loading steels high cycle fatigue failure mechanism |
| DOI | 10.3390/met13030511 |
| Indexed By | SCI |
| Language | 英语 |
| WOS ID | WOS:000959640600001 |
| WOS Research Area | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| WOS Subject | Materials Science ; Metallurgy & Metallurgical Engineering |
| Funding Organization | National Natural Science Foundation of China Basic Science Center [11988102] ; International Postdoctoral Exchange Fellowship Program (China) |
| Classification | 二类 |
| Ranking | 1 |
| Contributor | Sun, CQ (corresponding author), Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing 100190, Peoples R China. ; Sun, CQ (corresponding author), Univ Chinese Acad Sci, Sch Engn Sci, Beijing 100049, Peoples R China. |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://dspace.imech.ac.cn/handle/311007/91792 |
| Collection | 非线性力学国家重点实验室 |
| Affiliation | 1.Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing 100190, Peoples R China 2.Univ Chinese Acad Sci, Sch Engn Sci, Beijing 100049, Peoples R China |
| Recommended Citation GB/T 7714 | Li G,Liu, Jiajun,Sun, Jian,et al. Effects of Natural Aging and Discontinuous Cyclic Loading on High Cycle Fatigue Behavior of Steels[J]. METALS,2023,13,3,:511.Rp_Au:Sun, CQ (corresponding author), Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing 100190, Peoples R China., Sun, CQ (corresponding author), Univ Chinese Acad Sci, Sch Engn Sci, Beijing 100049, Peoples R China. |
| APA | 李根,Liu, Jiajun,Sun, Jian,&孙成奇.(2023).Effects of Natural Aging and Discontinuous Cyclic Loading on High Cycle Fatigue Behavior of Steels.METALS,13(3),511. |
| MLA | 李根,et al."Effects of Natural Aging and Discontinuous Cyclic Loading on High Cycle Fatigue Behavior of Steels".METALS 13.3(2023):511. |
| Files in This Item: | Download All | |||||
| File Name/Size | DocType | Version | Access | License | ||
| Jp2023A170.pdf（4884KB） | 期刊论文 | 出版稿 | 开放获取 | CC BY-NC-SA | View Download | |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment